Black matte epoxy electrophoretic paint for 3C electronics parts
Product Introduction
HL-1607LB/HL-1530G Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coatingthat isenvironment-friendly withhigh propertyandlow cost. Such coatingdoesnot contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, andcan adapt galvanized steel sheet perfectly,almost canbe applied to foundation coating of all metal, suchas: coldandhotrolledsteelsheet,galvanizedsteel sheetandstainless steelsheetetc
This product features shown below:
| Good stability of bath can adaptable for a longer updating cycle |
| High throwing power, internal and external uniformity. |
| Excellent leveling coating, good bonding for ceand compatibility with plastic powder |
Main ingredients:
Pigment: carbon black, kaolin, antirust pigment
Solvent: alcohol ether
Additives: surface active agent, prevent shrinkage cavity agent
Product quality data:
| Project | Technical data | Test standard | ||
| Resin (HL-1607LB) | Black Paste (HL-1530G) | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 1200.00
Paste 250.00
DI water 2000.00
Total 3250.00
⑵ Ripening conditions
Sample quantity: 3000～5000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)
Specification statement:
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Customers in the 3C industry:
 | |