High weatherability electrophoretic paint for Fluid equipment
|
HR-4000BLB Epoxy acrylic Color Cationic Electrocoat is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating.
|
|
This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating
|
|
such as:cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.
|
|
High penetration and good uniformity of internal and external.
|
Good stability of bath can adaptable for a longer updating cycle. |
|
The bath has strong anti-shrinkage and anti-pollution ability.
|
The appearance of the coating is flat, delicate, smooth. |
|
Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting system.
|
|
|
Pigment: Titanium pigment, Organic pigment, kaolin, antirust pigment
|
|
Additives: surface active agent, prevent shrinkage cavity agent
|
|
Curing agent: totally enclosed multi-isocyanates
|
|
Matrix resin: acrylic modified epoxy resin
|
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 70-90 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| Weather resistance | h,(film thickness ≥ 20μm) ,≥ | 500 | GB/T 1865 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 500 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Storage, packaging and transportation :
This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now