Low temperature curing electrophoresis paint for Compressor
Product Introduction :
|
OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating,
such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable
|
.
This product features shown below :
|
Good stability of bath can adaptable for a longer updating cycle
| High penetration and good uniformity of internal and external. |
|
Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material
| |
Main ingredients:
|
Additives: surface active agent, prevent shrinkage cavity agent
|
|
Pigment: carbon black, kaolin, antirust pigment
|
|
Neutralizing agent: organic acid
|
|
Matrix resin: Acrylic modified epoxy resin
|
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 1000.00 -1250.00
Paste 250.00
DI water 1000.00
Total 2250.00 -2500.00
(2)Ripening conditions
Sample quantity: 2250～2500g
Container: 4L (Diameter 16cm)
Tank temperature: 28~32℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions: (130-140)℃×(20-30)min (Keeping temperature of parts coated)
Specification statement
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Customer production site :