Electrophoretic coating for home appliance and household industry
Product Introduction
HS-6060LB/HS-2516G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
Main ingredients
Solvent: alcohol ether
Additives: surface active agent, prevent shrinkage cavity agent
Neutralizing agent: organic acid
Matrix resin: Acrylic modified epoxy resin
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HS-6060LB) | Gray Paste(HS-2516G) | |||
| Appearance | —— | Milky white liquid | Gray viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Bath on site management project
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:(3.5-4.5) | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day | |
| PH | 5.7-6.2 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1200±400 | 1500±500 | once a day | |
| P/B | 0.2-0.3 | once a week | ||
| L panel | Smooth horizontal plane and vertical plane without obvious differences | once a week | ||
| Solvent content (%) | 0.5-1.8 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥320 | once a week | ||
| Bath temperature ( ℃ ) | 28-35 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 170-185 | once a day | |
| Curing conditions | Drying temperature | (165-180)℃×(20-30)min (With content holding time) | once a day | |