Special furniture white electrophoresis paint
Product Introduction :
| HS-5500LB/HS-5500 White epoxy acrylic cathodic electrophoretic coating for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. and get the national invention patent and the Shanghai science and technology commission of high-tech transformation project. |
| It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, |
| such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc. |
This product features shown below:
|
The appearance of the coating is flat, delicate, smooth, and has a good hiding power for the substrate
|
Good stability of bath can adaptable for a longer updating cycle. | The bath has strong anti-shrinkage and anti-pollution ability. |
Main ingredients:
①,Neutralizing agent: organic acid
②,Pigment: titanium dioxide, kaolin,antirust pigment
③,Additives: surface active agent, prevent shrinkage cavity agent,resistance to yellowing agen
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 24 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 600 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Construction equipment
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now