Water borne paint for Pump
Cooperation Client Directory:Siemens；Wilo；Leybold; SNC
Advantages: High performance; Low VOCs
Product Specification
一,Product Introduction
Epoxy zinc-rich primer ET-0003A is a new generation waterborne acrylic finish paint researched and developed by HLS Paint (Shanghai) Co., Ltd.Low solvent content, no heavy metals such as lead, cadmium, chromium, mercury, etc. The paint film has good adhesion and good flexibility; this series of products has excellent corrosion resistance; it is suitable for different metal plates..
二,Scope of application
The product can be directly attached to the metal substrate; the upper coating is generally a matching water-based topcoat.
三,Product quality data
Original paint technical date
| Number | Project | Technical data | Test standard | |
| 1 | original | No agglomerate and impurities | Visual after stirring | |
| 2 | Viscosity | T-4,25℃,S | ≥90 | GB/T1723 |
| 3 | Fineness | μm | ≤30 | GB/T1724 |
| 4 | Hiding power | g/m2 | ≤140 | GBT 23986-2009 |
Notes: 1. GB is the national standard.
2. Above technical indicators and usage requirements indicators may be in the project, testing methods and performance index is different, the agreed amount shall prevail.
四,Construction technological parameter
1. Suitable substrate:Metal substrate such as cast iron and tinplate .
2. Mixture ratio
| Binder | Hardener | |
| Ratio (mass ratio) | 7 | 1 |
3. Suitable for construction environment temperature and humidity: Temperature 10-35℃, humidity:30-80%RH
4. Substrate processing: There is no oil pollution and dust particles of substrate
5. Applicable construction way: Air spraying, Airless spraying, Electrostatic spray.
6. Flow time:2-5min/10-35℃.
7. Curing conditions:70-80 ℃/ 30-40 min (workholding time).
8. Personnel protection: workers should wear personal protective equipment.
五,Precautions
1. Equipment cleaning can use diluted ammonia solution or matched cleaning agent.
2. It is harmful to health after inhaled. Please take when the construction security measures.
六,Storage, packaging and transportation
This product is a water-borne coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for the 20L / 50L / 100L / 200L plastic drum; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products. This product should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
一,Product Introduction
Epoxy intermediate coating ET-1001A is a new generation waterborne acrylic finish paint researched and developed by HLS Paint (Shanghai) Co., Ltd.Low solvent content, no heavy metals such as lead, cadmium, chromium, mercury, etc. The paint film has good adhesion and good flexibility; this series of products has excellent corrosion resistance; it is suitable for different metal plates..
二,Scope of application
The product can be directly attached to the metal substrate; the upper coating is generally a matching water-based topcoat.
三,Product quality data
Original paint technical date
| Number | Project | Technical data | Test standard | |
| 1 | original | No agglomerate and impurities | Visual after stirring | |
| 2 | Viscosity | T-4,25℃,S | ≥90 | GB/T1723 |
| 3 | Fineness | μm | ≤30 | GB/T1724 |
| 4 | Hiding power | g/m2 | ≤140 | GBT 23986-2009 |
Notes: 1. GB is the national standard.
2. Above technical indicators and usage requirements indicators may be in the project, testing methods and performance index is different, the agreed amount shall prevail.
四,Construction technological parameter
1. Suitable substrate:Metal substrate such as cast iron and tinplate .
2. Mixture ratio
| Binder | Hardener | |
| Ratio (mass ratio) | 7 | 1 |
3. Suitable for construction environment temperature and humidity: Temperature 10-35℃, humidity:30-80%RH
4. Substrate processing: There is no oil pollution and dust particles of substrate
5. Applicable construction way: Air spraying, Airless spraying, Electrostatic spray.
6. Flow time:2-5min/10-35℃.
7. Curing conditions:70-80 ℃/ 30-40 min (workholding time).
8. Personnel protection: workers should wear personal protective equipment.
五,Precautions
1. Equipment cleaning can use diluted ammonia solution or matched cleaning agent.
2. It is harmful to health after inhaled. Please take when the construction security measures.
六,Storage, packaging and transportation
This product is a water-borne coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for the 20L / 50L / 100L / 200L plastic drum; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products. This product should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
一,Product introduction
PT-2028 series two-component water-based polyurethane topcoat is a new generation of two-component water-based environmental protection topcoat developed by Haorisen Coatings (Shanghai) Co., Ltd .; it has low solvent content and does not contain lead, cadmium, chromium, mercury and other heavy metals. The paint film has the characteristics of good adhesion, good flexibility, etc. This series of products can be adjusted with various effects and colors to meet the design requirements of different products; it has excellent decoration and protection.
二,Scope of application
The product is mainly used for water-based epoxy primer / intermediate primer.
三,Technical index
3.1 Technical index of original paint
| Serial number | Project | Index | Inspection standards | |
| 1 | original | No agglomerate and impurities | Visual after stirring | |
| 2 | Viscosity | 涂-4,25℃,s | ≥30 | GB/T1723 |
| 3 | Fineness | μm | ≤10 | GB/T1724 |
| 4 | VOC content | g/L | ≤150 | GBT 23986 |
| 5 | Non-volatile matter content | % | ≥45 | GB/T 1725 |
| 6 | Proportion of original paint | kg/L | ≥1.1 | GB/T 6750 |
| 7 | Hiding power | g/m2 | ≤100 | GB/T 1726 |
Notes: 1. GB is the national standard.
2. Above technical indicators and usage requirements indicators may be in the project, testing methods and performance index is different, the agreed amount shall prevail.
四,Construction process parameters
1. Suitable substrate:Metal substrate such as cast iron and tinplate .
2. Mixture ratio
| Binder | Hardener | Water | |
| Ratio (mass ratio) | 4.0-6.0 | 1 | Right amount |
3. Suitable for construction environment temperature and humidity: Temperature 10-35℃, humidity:30-80%RH
4. Substrate processing: There is no oil pollution and dust particles of substrate
5. Applicable construction way: Air spraying, Airless spraying, Electrostatic spray.
6,Flow time:8-15min/10-35℃.
7,Curing conditions:70-80℃/20-40min(workholding time).
8. Personnel protection: workers should wear personal protective equipment.
五,Precautions
1. Equipment cleaning can use diluted ammonia solution or matched cleaning agent.
2. It is harmful to health after inhaled. Please take when the construction security measures.
六,Storage, packaging and transportation
This product is a water-borne coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for the 20L / 50L / 100L / 200L plastic drum; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products. This product should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
 | |
| |
| |
| |
| |
| |